Certification: | REACH |
---|---|
Environmental Protection: | Yes |
Color: | Grey |
Standard: | SGS ISO |
Ink Drying: | Oxidative Polymerization Drying |
Storage: | Cool Warehouse |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
model | YH-S516 | YH-300 | YH-300A | YH-300C | YH-300E |
Particle size | 3.0-4.0 | 3.2-4.2 | 3.2-4.2 | 3.2-4.2 | 3.2-4.2 |
Silica | >=98 | >=98 | >=98 | >=98 | >=98 |
(After burning)% | |||||
DBPOil absorption value cm3/g | 2.4-2.5 | 3.0-3.3 | 2.9-3.2 | 3.2-4.2 | 2.0-3.5 |
pH value | 6-8 | 6-8 | 6-8 | 6-8 | 5-8 |
Heating loss% | <=5 | <=5 | <=5 | <=5 | <=5 |
Ignition loss % | <=6 | <=6 | <=6 | <=6 | <=6 |
Porosity ml/g | 1.5 | 1.8 | 2 | 1.8 | 1.8 |
Surface treatment | without | without | without | Inorganic | Inorganic |
Type | Appearance | Specific surface area(BET) | PH-value | Loss on heating | Loss on ignition | Sieve residue | SiO2 content | Tamped density | Carbon content | Al2O3 mass fraction | TiO2 mass fraction | Fe2O3 mass fraction | Chloride content |
m2/g | Wt% | Wt% | (45μm) | Wt% | g/L | Wt% | mg/kg | mg/kg | mg/kg | mg/kg | |||
SS-150 | Fluffy white powder | 150±15 | 3.6-4.5 | <1.0 | <1.5 | <0.03 | >99.8 | 25-60 | <0.2 | ≤500 | ≤300 | ≤30 | |
SS-200 | 200±30 | 3.7-4.5 | ≤1.5 | ≤2.0 | ≤250 | >99.8 | ≤50 | ≤2.0 | ≤400 | ≤200 | ≤30 | ≤250 | |
SS-300 | 300±30 | 3.7-4.5 | ≤2.0 | ≤2.0 | ≤250 | >99.8 | ≤50 | ≤2.0 | ≤400 | ≤200 | ≤30 | ≤250 | |
SS-380 | 380±30 | 3.7-4.5 | ≤2.0 | ≤2.0 | ≤250 | >99.8 | ≤50 | ≤2.0 | ≤400 | ≤200 | ≤30 | ≤250 |
Item No | characteristics | properties | Properties | Unit | Typical Value | Applications |
BY-701 | BY-701 is surface-treated fumed silica with active silanol group modified by special silan. | Used as rheology control agent in composite liquid system; | Specific surface area, BET | m2/g | 150±15 | Paints & coatings |
PH value in 4% dispersion | / | 4.0-6.0 | Plastics & Elastomers | |||
Improve scratch resistance & abrasion resistance for paints & coatings ( UV coatings) | Loss on drying @ 105ºC×2h | wt.% | ≤1.5 | Dental composite materials | ||
Enhance mechanical properties, strength of composite materials and plastics | Loss on ignition @ 1000ºC×2h | wt.% | ≥4.5 | |||
SiO2 Content, based on ignited material |
wt.% | ≥99.8 | ||||
Carbon Content | wt.% | 4.5-6.5 |